Optical Upconversion Properties Of Tm2O3 / Yb2O3 Doped Lead Tellurite Glasses
DOI:
https://doi.org/10.55938/ijgasr.v2i1.38Keywords:
Melt-Quench, Absorption Spectra, Frequency up-ConversionAbstract
The melt-quench process was used to create the lead-tellurite glasses codoped with lanthanides as thulium and ytterbium. Thermal characterization carried by differential scanning calorimetry. X-ray diffraction is studies to get the nature of sold sample. The UV-Visible-IR absorption spectra was carried in range of 300 nm to 1100 nm. There were four unique absorption peaks on the glass thulium –ytterbium doped glass. The frequency up-conversion (UC) fluorescence has been seen at room temperature by 975 nm excitation.
Downloads
References
Dejneka, M. J. 1998, Mater. Res. Soc. Bull. 23, 57; and references therein. DOI: https://doi.org/10.1557/S0883769400031018
Höland, W., and Beall, G. 2002, Glass-Ceramic Technology, The American Ceramic Society.
Clara Gonçalves, M., Santos, L. F., and Almeida, R. M. 2002, C. R. Chimie, 5, 845. DOI: https://doi.org/10.1016/S1631-0748(02)01457-1
Adam, J.-L. 2001, J. Non-Cryst. Solids, 287, 401; Ibid. 2002, Chem. Rev., 102, 2461.
Beall, G.H., and Duke, D.A. 1983, “Glass-ceramic Technology” in “Glass Science and Technology”, vol. 1, Academic Press, New York, p. 403.
Auzel, F., Pecile, D., and Morin, D. 1975, J. Electrochem. Soc., 122, 101. DOI: https://doi.org/10.1149/1.2134132
Wang, Y., and Ohwaki, H. 1993, Appl. Phys. Lett., 63, 3268. DOI: https://doi.org/10.1063/1.110170
Tick, P. A., Borrelli, N. F., and Reaney, I. M. 2000, Opt. Mat., 15, 81. DOI: https://doi.org/10.1016/S0925-3467(00)00017-3
Méndez-Ramos, J., Lavín, V., Martín, I. R., Rodríguez-Mendoza, U. R., Rodríguez, V. D., Lozano-Gorrín, A. D., and Núñez, P. 2001, J. Appl. Phys., 89, 5307; Ibid. 2003, J. Appl. Phys., 94, 2295.
Abril, M., Méndez-Ramos, M., Martín, I. R., Rodríguez-Mendoza, U. R., Lavín, V., Delgado-Torres, A., Rodríguez, V. D., Núñez, P., and LozanoGorrín, A. D. 2004, J. Appl. Phys., 95, 5271.
Fernández, J., Balda, R., Mendioroz, A., Sanz, M., Adam, J.-L. 2001, J. NonCryst. Solids, 287, 437. DOI: https://doi.org/10.1016/S0022-3093(01)00597-X
Scheps, R. 1996, Prog. Quant. Electr., 20, 271. DOI: https://doi.org/10.1016/0079-6727(95)00007-0
Joubert, M.-F. 1999, Opt. Mat., 11, 181; and references therein. DOI: https://doi.org/10.1016/S0925-3467(98)00043-3
QuintanillaM, NúñezNO, CantelarE, Ocaña M, Cussó F. J Appl Phys. 2013;113(17):174308. DOI: https://doi.org/10.1063/1.4803540
Albalawi A, Varas S, Chiasera A, Gebavi H, Albalawi W, Blanc W,. Opt Mater Express. 2017;7(10):3760 DOI: https://doi.org/10.1364/OME.7.003760
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Ghizal F. Ansaria, S. P. Mahato
This work is licensed under a Creative Commons Attribution 4.0 International License.